Experimental

Five coated papers for rotogravure, of about the same grammage, were used in this experiment. The characteristics of the papers are reported in Table 1.

Grammage, Print-Surf (PPS) roughness, Gloss, and PPS porosity were measured according to TAPPI standards (TAPPI, 1999, 2002). A PPS Model 90 (Messmer Instrument) was used for roughness and porosity measurements. A Gardco® Novo-GlossTM Glossmeter was used for gloss measurements. Pore sizes were determined by mercury porosimetry. Measurements were carried out using an Autopore IV 9500 (Micromeritics Instrument). More details can be found in a

previous paper (Xu et al., 2005).

The papers were printed on a Cerutti rotogravure web press (Cerutti Model 118, Italy), located at Western Michigan University (WMU) Printing Pilot Plant. Commercial toluene-based coated yellow, magenta, and cyan inks for rotogravure (Flint Ink) were used. All inks were doped with a selected tracer.

The ink efflux time with Shell cup #2 was kept at 21 ± 0.5 seconds for all inks. Printing was done at 1000 ft/min with electrostatic assist (ESA) on. The magenta cylinder has elongated cells, while the cyan cylinder has compressed cells.

Количество переданной краски и следовательно количества краски на бумаге было определено различием веса печатного цилиндра до и после печати. Поэтому, эти модели не могут быть применены к поведению красочного слоя других типов красок.

Был изучен новый метод измерения толщины красочного слоя. Краски лакировались с трассирующим снарядом, который использовался, чтобы вычислить массу передачи краски, и следовательно толщину слоя. Этот внутренний метод трассирующего снаряда может использоваться во всех видах красок, включая флексографские и краски для глубокой печати на основе растворителя.

Цели этой работы состояли в том, чтобы использовать внутренний метод трассирующего снаряда, иметь размеры толщин, найти лучшую модель соответствующую экспериментальным данным и изучить коэффициенты регресса.